摘 要

以水合硝酸鋅（Zn(NO3)2•6H2O）和氫氧化鈉（NaOH）為主要原料，通過(guò)添加一種表面活性劑十二烷基苯磺酸鈉（SDBS），100℃水熱條件下合成了一種粉體。該粉體經(jīng)X射線衍射（XRD）分析具有氧化鋅（ZnO）結(jié)構(gòu)；掃描電鏡（SEM）和透射電鏡（TEM）分析表明：粉體是一種針狀的納米晶須，其顯著特點(diǎn)是晶須無(wú)論長(zhǎng)短粗細(xì)，都具有一頭尖一頭鈍的針狀形貌。納米晶須的平均長(zhǎng)度約為3微米（μm），平均直徑約130納米（nm），長(zhǎng)徑比為25左右。文章還研究了其紫外-可見(jiàn)（UV-vis）吸收性能，并探討了針狀氧化鋅納米晶須可能的生長(zhǎng)機(jī)制。
關(guān)鍵詞：針狀氧化鋅；納米晶須；溫和水熱合成；光學(xué)性能

ABSTRACT

Hydrothermal is effective method to prepare fine material especially crystal; zinc oxide is a kind of materials which have a very wide range useful. In this paper, hydrated zinc nitrate and sodium hydroxide as raw material, by adding a surfactant, at 100 ℃ under the conditions of the hydrothermal synthesize fine powders. XRD and SEM show that: it is zinc oxide powder; the product withnot adding surfactants is needle-like morphology; the product derived with surfactant show hexagonal columnar short. The article also discussed the application of zinc oxide material.
Keyword :Fine zinc oxide; Hydrothermal synthesis; Morphology

目 錄
1 緒 論 1
1.1 引言 1
1.2 ZnO的性質(zhì) 1
1.3 ZnO的晶體結(jié)構(gòu) 2
1.4 ZnO的性能及應(yīng)用 3
1.4.1催化及光催化領(lǐng)域 4
1.4.2光、電及氣敏等領(lǐng)域 4
1.4.3日用化工及生物醫(yī)學(xué)領(lǐng)域 5
1.5 納米ZnO的制備技術(shù) 6
1.5.1 溶膠 -凝膠法 6
1.5.2 直接沉淀法 7
1.5.3 均勻沉淀法 7
1.5.4 微乳液法（反相膠束法） 7
1.3.5 水熱法 8
1.6 ZnO晶體的研究進(jìn)展及現(xiàn)狀 8
1.6.1 ZnO晶體的研究進(jìn)展 8
1.6.2 ZnO晶體國(guó)外研究現(xiàn)狀 9
1.6.3 ZnO晶體國(guó)內(nèi)研究現(xiàn)狀 10
1.6.4存在的問(wèn)題 10
1.7 本課題研究的目的 10
2 實(shí)驗(yàn)部分 11
2.1 實(shí)驗(yàn)儀器及試劑 11
2.1.1 實(shí)驗(yàn)儀器 11
2.1.2 實(shí)驗(yàn)試劑 11
2.2 實(shí)驗(yàn)設(shè)計(jì) 11
2.2.1 實(shí)驗(yàn)原理 11
2.2.2 實(shí)驗(yàn)方法 11
2.2.3實(shí)驗(yàn)步驟 11
2.3 產(chǎn)物表征 12
2.4 結(jié)果與討論 12
2.4.1 產(chǎn)物的結(jié)構(gòu)分析 12
2.4.2 產(chǎn)物的形貌分析 12
2.4.3 表面活性劑的影響 15
2.4.4 討論 15
3 結(jié)論 16
參考文獻(xiàn) 17
致 謝 18